Burst strength and impact performance on glass fibre reinforced epoxy (GRE) composite pipes/
The GRE composite pipes are commonly produced by the filament winding technique. After the composite specimens were cut into required size, it was immersed in 80C water for periods of 500, 1000, and 1500 h to simulate the ageing effects. An instrumented impact testing machine with the drop weight sy...
Wedi'i Gadw mewn:
| Prif Awdur: | |
|---|---|
| Awdur Corfforaethol: | |
| Fformat: | Traethawd Ymchwil Llyfr |
| Iaith: | English |
| Cyhoeddwyd: |
Perlis, Malaysia
School of Mechatronic Engineering
2016
|
| Tagiau: |
Ychwanegu Tag
Dim Tagiau, Byddwch y cyntaf i dagio'r cofnod hwn!
|
| LEADER | 02106ntm a2200373Ii 4500 | ||
|---|---|---|---|
| 001 | vtls000139150 | ||
| 003 | MY-ArUMP | ||
| 005 | 20210731032627.0 | ||
| 008 | 200204s2016 my a f bm 000 0 eng d | ||
| 035 | |a (OCoLC)1138938047 | ||
| 035 | |a (OCoLC)on1138938047 | ||
| 039 | 9 | |a 202002041619 |b SMI |c 202002041618 |d SMI |c 202002041559 |d SMI |y 202002041554 |z SMI | |
| 040 | |a MYPMP |b eng |e rda |c MYPMP | ||
| 049 | |a MYPA | ||
| 100 | 0 | |a Hawa Ahmad | |
| 245 | 1 | 0 | |a Burst strength and impact performance on glass fibre reinforced epoxy (GRE) composite pipes/ |c Hawa Binti Ahmad |
| 264 | 1 | |a Perlis, Malaysia |b School of Mechatronic Engineering |c 2016 | |
| 300 | |a xiv, 110 pages |b colour illustration |c 30 cm. | ||
| 336 | |a text |b txt |2 rdacontent | ||
| 337 | |a unmediated |b n |2 rdamedia | ||
| 338 | |a volume |b nc |2 rdacarrier | ||
| 502 | |a Thesis (Master of Science) -- Universiti Malaysia Perlis. School of Mechatronic Engineering, 2016 | ||
| 504 | |a Includes bibliographical references. | ||
| 520 | |a The GRE composite pipes are commonly produced by the filament winding technique. After the composite specimens were cut into required size, it was immersed in 80C water for periods of 500, 1000, and 1500 h to simulate the ageing effects. An instrumented impact testing machine with the drop weight system was used to carry out the impact tests. Then the impacted specimens proceed with internal hydrostatic monotonic burst tests to determine the deformation behaviour of the composite pipes. Scanning electron microscopy (SEM) was used to analyse and characterize the inner and outer surface of the damage pipe wall. | ||
| 541 | |a Gift from Centre for Graduate Studies (Master of Science) |b 2017 | ||
| 710 | 2 | |a Universiti Malaysia Perlis | |
| 790 | 1 | |a School of Mechatronic Engineering | |
| 791 | 1 | |a Master of Science | |
| 792 | 1 | |a 2016 | |
| 942 | |2 lcc |c BK-TD | ||
| 949 | |a VIRTUAITEM |d 30000 |f 1 |x 901 |6 054066 | ||
| 994 | |a C0 |b MYPMP | ||
| 999 | |c 20006 |d 20006 | ||
| 952 | |0 0 |1 0 |2 lcc |4 0 |6 TA04189 C6 H389 02016 F RB |7 0 |9 25346 |a PTSFP |b PTSFP |c 6 |d 2021-07-31 |o TA418.9 C6H389 2016 f rb |p 054066 |r 2021-07-31 |t 1 |w 2021-07-31 |y BK-TD | ||