Analysis of binary aluminium-tin products with varying compositions and optimum flowability, tensile strength and hardness
This final year project is about investigation, in the first stage aluminium tin was melt in electric furnace and the melting was done at 550 ℗ʻC as it was to make sure that resulted in better wettability of aluminium tin particles and reduced entrapment of gases in the cast. The second part of this...
Saved in:
| Hovedforfatter: | |
|---|---|
| Format: | Electronisk Software Database |
| Sprog: | English |
| Fag: | |
| Tags: |
Tilføj Tag
Ingen Tags, Vær først til at tagge denne postø!
|
| LEADER | 01482nmi a2200241 a 4500 | ||
|---|---|---|---|
| 001 | vtls000053028 | ||
| 003 | MY-KaKUK | ||
| 005 | 20210816100434.0 | ||
| 007 | co bg llla | ||
| 008 | 111129s2008 my f d eng d | ||
| 039 | 9 | |a 201111291745 |b VLOAD |c 201008201531 |d AYAR |c 200909101208 |d RAR |y 200905121140 |z SNSA | |
| 090 | 0 | 0 | |a TN665 |b B2K45 2008 |
| 100 | 0 | |a Mohammad Khairol Kamal. |e author | |
| 245 | 1 | 0 | |a Analysis of binary aluminium-tin products with varying compositions and optimum flowability, tensile strength and hardness |h [electronic resource] / |c Mohammad Khairol Kamal. |
| 264 | 0 | |a Perlis, Malaysia |b School of Materials Engineering, Universiti Malaysia Perlis |c 2008. | |
| 300 | |a 1 CD-ROM |c 4 3/4 in. | ||
| 500 | |a Final Year Project | ||
| 520 | |a This final year project is about investigation, in the first stage aluminium tin was melt in electric furnace and the melting was done at 550 ℗ʻC as it was to make sure that resulted in better wettability of aluminium tin particles and reduced entrapment of gases in the cast. The second part of this investigation involved evaluation of microstructure and properties of this aluminium in as cast and heat treated conditions. | ||
| 650 | 0 | |a Metallurgy. | |
| 949 | |a VIRTUAITEM |d 30000 |f 1 |x 701 |6 902000298 |a TN665 B2K45 2008 | ||
| 942 | |2 lcc |c COMPFILE | ||
| 999 | |c 93991 |d 93991 | ||
| 952 | |0 0 |1 0 |2 lcc |4 0 |6 TN0665 B2 K45 02008 |7 0 |9 91800 |a PTSFP |b PTSFP |c 8 |d 2021-08-16 |l 0 |o TN665 B2K45 2008 |p 902000298 |r 2021-08-16 |t 1 |w 2021-08-16 |y COMPFILE | ||