Effects of T6 treatment on the microstructural changes, hardness and thermal analysis of As-Cast Al-Si-Mg alloys
Aluminium-silicon-magnesium is usually applied in automotive industry such as in block engine. The main objective of this final year project is to study the changes in microstructure, hardness and the thermal analysis curve after the sample were processed starting from as received, as-cast, solution...
Պահպանված է:
| Հիմնական հեղինակ: | |
|---|---|
| Ձևաչափ: | Էլեկտրոնային Ծրագրային ապահովում Շտեմարան |
| Լեզու: | English |
| Խորագրեր: | |
| Ցուցիչներ: |
Ավելացրեք ցուցիչ
Չկան պիտակներ, Եղեք առաջինը, ով նշում է այս գրառումը!
|
| Ամփոփում: | Aluminium-silicon-magnesium is usually applied in automotive industry such as in block engine. The main objective of this final year project is to study the changes in microstructure, hardness and the thermal analysis curve after the sample were processed starting from as received, as-cast, solution treatment at 5100C for four hours and quenched in the iced water. |
|---|---|
| Նյութի նկարագրություն: | Final Year Project |
| Ֆիզիկական նկարագրություն: | 1 CD-ROM 4 3/4 in. |